Abstract
The phase equilibria of the Sb2Te2S-Bi2Te2S system was studied by powder X-ray diffraction (PXRD), differential thermal analysis (DTA), scanning electron microscope (SEM) and energy dispersive X- ray (EDX) microanalysis. It was shown that due to incongruent melting of the Sb2Te2S compound the system is non-quasibinary, but it is stable below the solidus and characterized by the formation of a continuous series of solid solutions with a tetradymite-like hexagonal structure. The lattice parameters were determined from powder diffraction patterns. It was established that the crystal lattice parameters of solid solutions vary linearly with composition.